Additional Information:
A nickel-chromium precipitation-hardening alloy suited for high strength at temperatures above 1300 F, with useful strength up to 1800 F. The alloy is also has excellent properties and ductility at cryogenic temperatures.
APPLICATIONSStructural members in hot sections of gas turbines such as discs, thrust reversers and ducts. Heat treat fixtures and cryogenic vessels, springs and fasteners.
MACHINABILITYConventional machining techniques used for iron based alloys may be used. This alloy does work-harden during machining and has higher strength and “gumminess” not typical of steels. Heavy duty machining equipment and tooling should be used to minimize chatter or work-hardening of the alloy ahead of the cutting.
Chemical Composition,%
Nickel (plus Cobalt)....................................................70.00 min. Chromium...................................................................14.0-17.0 Iron..................................................................................5.0-9.0 Titanium.......................................................................2.25-2.75 Aluminum....................................................................0.40-1.00
Niobium (plus Tantalum)..............................................0.70-1.20 Manganese.................................................................1.00 max. Silicon.........................................................................0.50 max. Sulfur...........................................................................0.01 max. Copper........................................................................0.50 max. Carbon........................................................................0.08 max.
Cobalt1 .......................................................................1.00 max
SIZE 6MM TO 200MM DIA ROUND BAR.
SIZE 1MM TO 100MM THICKNESS PLATE.
SIZE 6MM TO 350MM OD PIPE .
SIZE 0.5MM TO 6MM DIA WIRE.
.AVAILABLE IN STOCK.
Additional Information:
Incoloy™ 925 offers exceptional strength up to 1000°F (538°C). It’s a nickel-iron-chromium, age-hardenable alloy ideal for applications that require resistance to corrosion and pitting. Machinable and weldable, Incoloy™ 925 can be not and cold worked.
CHEMICAL COMPOSITION OF INCOLOY™ 925SIZE 6MM TO 200MM DIA ROUND BAR.
SIZE 1MM TO 100MM THICKNESS PLATE.
SIZE 6MM TO 350MM OD PIPE .
SIZE 0.5MM TO 6MM DIA WIRE.
.AVAILABLE IN STOCK.
Additional Information:
Incoloy™ 925 offers exceptional strength up to 1000°F (538°C). It’s a nickel-iron-chromium, age-hardenable alloy ideal for applications that require resistance to corrosion and pitting. Machinable and weldable, Incoloy™ 925 can be not and cold worked.
CHEMICAL COMPOSITION OF INCOLOY™ 925SIZE 6MM TO 200MM DIA ROUND BAR.
SIZE 1MM TO 100MM THICKNESS PLATE.
SIZE 6MM TO 350MM OD PIPE .
SIZE 0.5MM TO 6MM DIA WIRE.
.AVAILABLE IN STOCK.
This nickel-chromium-molybdenum wrought alloy is an excellent general purpose material for elevated temperature use in high strength, oxidation problem applications. It also has excellent corrosion resistance to many acids and resists intergranular attack and stress-corrosion cracking.
FORGING APPLICATIONSThe alloy finds use in high temperature applications such as heat exchangers and gas turbine components. Because of its good corrosion resistance it is also used in wet scrubbers and some acid process equipment.
MACHINABILITYMay be machined by conventional means. However the alloy tends to work harden ahead of cutting and rigid tooling is essential to avoid chatter and work hardening in front of the tool edge.
FORMINGThis alloy can be cold formed by conventional means and tooling. The alloy does work harden during cold working with an attendant increase in strength. This increase in strength may be of value for moderate temperature applications and, in these instances, the formed parts can be left in the cold work hardened condition.
WELDINGWelding is readily accomplished using matching alloy filler metal for the conventional welding techniques.
HEAT TREATMENTThe alloy is furnished in the solution annealed condition. This is done at 2150 F for sufficient time dependent upon section thickness. Following the anneal the alloy may be air cooled.
FORGINGHot forging can be done by heating the billet to 2100 – 2150 F, but not over 2150. Heavy forging may then be done down to a billet temperature of 1850 F and light forging down to 1700 F. Final reductions of 15 to 20% minimum are recommended to maintain
HOT WORKINGHot forming may be done by heating the alloy to 2150 F. Because this alloy is engineered for good strength at high temperatures it will resist hot deformation and therefore requires powerful equipment to perform hot forming.
COLD WORKINGThe alloy can be cold formed by conventional methods and tooling. See also the comments under “Forming” regarding work hardening.
ANNEALINGBecause the alloy work hardens during hot or cold forming it may be necessary to anneal such parts in order to complete forming operations. Annealing is done at 1800 to 2000 F and air cooled. Stress relief of cold worked parts may be accomplished at 110.
SIZE 6MM TO 200MM DIA ROUND BAR.
SIZE 1MM TO 100MM THICKNESS PLATE.
SIZE 6MM TO 350MM OD PIPE .
SIZE 0.5MM TO 6MM DIA WIRE.
.AVAILABLE IN STOCK.
Additional Information:
SIZE 6MM TO 200MM DIA ROUND BAR.
SIZE 1MM TO 100MM THICKNESS PLATE.
SIZE 6MM TO 350MM OD PIPE .
SIZE 0.5MM TO 6MM DIA WIRE.
Additional Information:
With a high creep and rupture strength to 1400°F (760°C), Incoloy™ 901is a nickel-iron-chromium alloy ideally suited for gas turbine and aircraft applications. Because of its high nickel content, it can be joined with ferritic alloy steels without thermal expansion provisions.
CHEMICAL COMPOSITION OF INCOLOY™ 901SIZE 6MM TO 200MM DIA ROUND BAR.
SIZE 1MM TO 100MM THICKNESS PLATE.
SIZE 6MM TO 350MM OD PIPE .
SIZE 0.5MM TO 6MM DIA WIRE.
.AVAILABLE IN STOCK.
Additional Information:
Inconel 713C offers outstanding resistance to thermal fatigue and good castability while offering exceptional rupture strength at 1700°F (927°C). Inconel 713C is a nickel-chromium alloy that is ideally suited for jet engine gas turbine blades.
CHEMICAL COMPOSITION OF INCONEL™ 713CSIZE 6MM TO 200MM DIA ROUND BAR.
SIZE 1MM TO 100MM THICKNESS PLATE.
SIZE 6MM TO 350MM OD PIPE .
SIZE 0.5MM TO 6MM DIA WIRE.
.AVAILABLE IN STOCK.
Additional Information:
SIZE 6MM TO 200MM DIA ROUND BAR.
SIZE 1MM TO 100MM THICKNESS PLATE.
SIZE 6MM TO 350MM OD PIPE .
SIZE 0.5MM TO 6MM DIA WIRE.
Additional Information:
SIZE 6MM TO 200MM DIA ROUND BAR.
SIZE 1MM TO 100MM THICKNESS PLATE.
SIZE 6MM TO 350MM OD PIPE .
SIZE 0.5MM TO 6MM DIA WIRE.
Additional Information: